ansys等效彈性變形的案例
通過(guò)ansys利用均勻化理論計(jì)算復(fù)合材料等效性能--等效彈性模量，剪切模量等
/PREP7
*SET,ALPH,0.5
*SET,TEMP,1
a=100
c1=0.4988
c2=1-c1
r1=sqrt(c1*a*a/3.1415926*4)
ET,1,PLANE42
KEYOPT,1,3,2
MP,EX,1,83.3
MP,PRXY,1,0.22
MPTEMP,,,,,,,,
MPTEMP,1,0
UIMP,1,REFT,,,
MPDATA,ALPX,1,,ALPH
MPDATA,ALPY,1,,-ALPH
MPDATA,ALPZ,1,,0
MP,EX,2,3.33
MP,PRXY,2,0.35
MPTEMP,,,,,,,,
MPTEMP,1,0
UIMP,1,REFT,,,
MPDATA,ALPX,2,,ALPH
MPDATA,ALPY,2,,-ALPH
MPDATA,ALPZ,2,,0
RECTNG,0,a,0,a,
PCIRC,r1, ,0,90,
AOVLAP,all
wpro,-45.000000,,
wpro,,,-90.000000
asbw,4
WPCSYS,-1,0
WPROTA,-45
CSWPLA,11,0,1,1,
CSYS,11
lsel,s,,,2,4
lsel,a,,,6
LESIZE,ALL, , ,11, ,1, , ,1,
lsel,s,,,10,11
lsel,a,,,1
LESIZE,ALL, , ,6, ,1, , ,1,
lsel,s,,,8,9
LESIZE,ALL, , ,22, ,1, , ,1,
allsel,
TYPE,1
MAT,1
ESYS,11
MSHAPE,0,2D
MSHKEY,0
amesh,3
TYPE,1
MAT,2
ESYS,11
MSHAPE,0,2D
MSHKEY,1
amesh,1,2
展開(kāi) Ansys Workbench 膠粘凝固過(guò)程，變形等效仿真 ￥15
針對(duì)階段1的膠層固化反應(yīng)體積收縮，同樣等效為溫度變化導(dǎo)致的體積變化，仍為降溫體積收縮仿真。這里需要考慮的重點(diǎn)是體積收縮量和等效降溫溫度的對(duì)應(yīng)關(guān)系。
階段1溫度：equivalent Temperature T1：利用降溫，等效膠層固化體積收縮。
? 根據(jù)膠體part體積收縮率Vs=0.02，計(jì)算當(dāng)量溫度T1；
? 體積收縮Vs 換算線收縮率Ls：Ls = 1-(1-Vs)^1/3; 由Vs=(V-V`)/V=(L3-(L-Ls)3)/L3；
? 線收縮量Ls 換算階段1當(dāng)量溫度：T1 = Tr-Ls/α； 由 (Tr-T1)*α*1 = Ls；
階段2溫度：equivalent Temperature T2：降溫體積縮小。
? 根據(jù)膠體part ：Tc 和Tr 差值，計(jì)算當(dāng)量溫度；
? 階段2當(dāng)量溫度：T2=T1-(Tc-Tr);
上述過(guò)程在一個(gè)static mechanical中可以通過(guò)Command命令的方式，利用BF命令定義節(jié)點(diǎn)溫度的方式，完成等效仿真模擬。大致流程如下：
? 用戶需要?jiǎng)?chuàng)建膠層為獨(dú)立part；
? 正常設(shè)置各部件的材料和連接方式。膠層的材料：固化后的材料屬性，建立線彈性模型即可；
? 在named selection 中選擇需要分析的膠層part體；
? 插入command命令更改輸入?yún)?shù)，計(jì)算；
本文這里在command中定義膠層新材料時(shí)，只設(shè)定了膠層的彈性模量這一個(gè)參數(shù)隨溫度而變化。